摘  要:本文是以N-羟甲基丙烯酰胺（NMA）为交联单体，丙烯酸正丁酯（BA）为主单体，过硫酸铵（APS）为引发剂，合成了P(NMA-AA-BA) 无皂乳液，并探究了丙烯酸（AA）用量对乳液稳定性能和成膜性能的影响。结果表明：在N-羟甲基丙烯酰胺投料量为10%的条件下，丙烯酸投料量为20%时，可制得最为稳定的无皂乳液；乳胶膜的交联度随分子链中AA链段含量的增加而升高，IR分析表明AA链段参与了交联反应。

Abstract:In this paper, N-methylol acrylamide (NMA) as the functional monomer, n-butyl acrylate (BA) as the main monomer, and ammonium persulfate (APS) as the initiator, explored the amount of acrylic acid (AA) The stability of the emulsion and the effect of film formation, and the formation of a high solids, stable acrylic soap-free emulsion with hydrophilic and lipophilic properties. The results showed that the increase of acrylic acid content increased the cross-linking degree of the film under the condition of 10% N-methylol acrylamide, and the dilution stability and salt resistance were the best when the acrylic acid content was 20%. 

关键字：无皂乳液聚合； N-羟甲基丙烯酰胺； 丙烯酸丁酯

Keywords: soap-free emulsion polymerization;  N-methylol acrylamide;  butylacrylate

目录

1、前言 4

2、实验 5

2.1实验仪器 5

2.2实验试剂 6

2.3无皂乳液的制备 6

2.4性能测试 6

2.4.1乳液耐水性测定 6

2.4.2乳液耐盐性测定 7

2.4.3乳液薄膜的溶胀度和溶失率 7

2.4.4聚合物分子量的测定 7

2.4.5乳液红外光谱分析 7

3、结果与讨论 7

3.1无皂乳液的制备 7

3.1.1反应pH对乳液稳定性影响 7

3.1.2引发剂含量对乳液稳定性影响 8

3.1.3投料比对乳液稳定性影响 8

3.1.4 GPC测量结果分析 9

3.1.5红外谱图测量结果分析 9

3.2影响薄膜性能的因素 10

3.2.1交联时间对薄膜性能的影响 10

3.2.2交联温度对薄膜性能的影响 11

3.2.3交联pH对薄膜性能的影响 12

3.3 交联机理 12

4、结论 13

5、参考文献 14

6、致谢 15

1、前言

无皂乳液是指在反应过程当中完全不添加乳化剂或只加入微量乳化剂（浓度小于临界胶束浓度）聚合而成的乳液[1]。与传统的乳液相比，无皂乳液具有所含乳胶粒粒径分布窄，无乳化剂添加等优点，因此应用前景十分广阔。

由于无皂乳液基本无乳化剂的添加，不仅在批量生产中降低了乳化剂的成本，还能有效避免因后处理脱除乳化剂所需的人工和物力成本。此外，无皂乳液的乳胶粒表面相比传统乳液粒更为洁净。由于乳化剂易从颗粒上解吸并在成膜时和成膜后发生迁移，使得薄膜性能下降，例如光泽度变低，对底物的粘附性变差和耐水性变差，而通过无皂乳液聚合可以降低该类事件发生的几率。因无皂乳液表面具有多种功能性基团，所以还可以制备单分散的功能性微球，除了在医学、化工中[2-3]可以用于临床检验诊断的计数、催化剂的载体等，在涂料生产中还可作手套、无纺布等其他包装材料的涂饰材料[4-5]。 P(NMA-BA)无皂乳液的制备及性能研究:http://www.chuibin.com/huaxue/lunwen_205555.html